Title: Structural studies of synthesis of CdSe from Cd/Se bilayer
Authors: Chauhan, A R
Mahadkar, A
Gaikwad, D
Patel, A P
Keywords: CdSe films
Wrutzite structure
Rapid thermal annealing
Issue Date: Oct-2006
Publisher: CSIR
Series/Report no.: C30B
Abstract: Cadmium and selenium bilayer have successfully been made by a vacuum evaporation technique on cleaned glass substrates under the vacuum of the order of 10-5mbar. The samples of different thicknesses were prepared by varying Cd:Se ratio as 1:1, 1:1.5,1:2. Rapid thermal annealing (RTA) of some bilayers have been carried out at different temperatures in nitrogen ambient. XRD measurements were made for structural analysis on these as-deposited and annealed samples. RTA studies could show the formation of cadmium selenide at the interface after annealing. XRF measurements were carried out for elemental analysis of these bilayers. XRF studies reveal that the films are found to be cadmium rich at room temperature. The results of CdSe formed from Cd/Se bilayer by RTA are compared with annealed sample.
Description: 777-781
ISSN: 0975-1041 (Online); 0019-5596 (Print)
Appears in Collections:IJPAP Vol.44(10) [October 2006]

Files in This Item:
File Description SizeFormat 
IJPAP 44(10) 777-781.pdf248.56 kBAdobe PDFView/Open

Items in NOPR are protected by copyright, with all rights reserved, unless otherwise indicated.