Title: Piezoelectric Properties of Ta (≤ 5 (mole)%) Doped in Na0.685K0.315NbO3
Authors: Negi, Jyotsana
Biswas, Don
Panwar, N S
Keywords: NKN;Ferroelectrics;Piezoelectric
Issue Date: Nov-2021
Publisher: NIScPR-CSIR, India
Abstract: To explore the piezoelectric potential of Ta doping on the MPB- like composition Na0.685K0.315NbO3, ceramic pellets of Na0.685K0.315Nb1-yTayO3 (y ≤ 0.05) were arranged by solid-state reaction method. For piezoelectric measurements, sintered pellets were electroded, in parallel capacitor configuration, with silver coating deposited by direct current (dc) magnetron sputtering of a silver target. Polarization and piezoelectric parameters were measured using a ferroelectric (PE- loop tracer) and piezo- meter (AixACCT Systems, GmbH). Composition (y) variation of remnant polarization, coercive field, converse piezoelectric coefficient (d*33), and polarization current measurements were carried out in the prepared compositions. The remnant polarization (Pr) is 18.439 μC/cm2 with a coercive field (Ec) of 8 kV/cm for NKNT single crystals. d*33 was observed 300.76 pm/V for y = 0.04 at the applied field of 22kV/cm.
Page(s): 740-743
URI: http://nopr.niscair.res.in/handle/123456789/58626
ISSN: 0975-0959 (Online); 0301-1208 (Print)
Appears in Collections:IJPAP Vol.59(11) [November 2021]

Files in This Item:
File Description SizeFormat 
IJPAP 59(11) 740-743.pdf1.11 MBAdobe PDFView/Open


Items in NOPR are protected by copyright, with all rights reserved, unless otherwise indicated.