Title: Mechanical properties and kinetics of boride layers on AISI D2 steel produced by plasma paste boriding
Authors: Keddam, Mourad
Makuch, Natalia
Kulka, Michal
Miklaszewski, Andrzej
Keywords: Plasma paste boriding;Kinetics;Borides;Activation energy;Adhesion test;Fracture toughness
Issue Date: Apr-2020
Publisher: NISCAIR-CSIR, India
Abstract: In the present study, the AISI D2 steel has been treated by the plasma paste boriding process using a gas mixture of 70% H2-30% Ar with 70% of borax and 30% SiC. The boriding treatment has been carried out at 700, 750 and 800 °C for an exposure time of 3 to 7 h. The plasma paste borided samples have been investigated by various techniques such as scanning electron microscopy, optical microscopy, XRD analysis, micro-hardness Vickers and the rockwell-C adhesion tests. The fracture toughness has also been measured on the plasma paste borided samples under different values of indentation load. From a kinetic point of view, the boride layers have obeyed the parabolic growth law. The value of boron activation energy for AISI D2 steel has been estimated as 130 kJ mol–1 using our experimental results. In addition, this obtained activation energy has been compared to the literature data.
Page(s): 221-233
ISSN: 0975-1017 (Online); 0971-4588 (Print)
Appears in Collections:IJEMS Vol.27(2) [April 2020]

Files in This Item:
File Description SizeFormat 
IJEMS 27(2) 221-233.pdf850.87 kBAdobe PDFView/Open

Items in NOPR are protected by copyright, with all rights reserved, unless otherwise indicated.