Title: Novel composite meshes to evaluate their structural property and in vivo biocompatibility for tissue repair
Authors: Lu, Yao
Fu, Shaoju
Hu, Bing
Cheng, Ge
Li, Nannan
Zhou, Shuanglin
Keywords: Biocompatibility;Electrospinning;Elctro-mesh;Interlocking texture;Inter-mesh;Pelvic floor repair;Polypropylene mesh;Polylactic acid mesh
Issue Date: Dec-2019
Publisher: NISCAIR-CSIR, India
Abstract: Composite meshes of different types have been prepared and used for tissue repair in pelvic floor disorder. An interlocking texture mesh (inter-mesh) and a membrane coated mesh (electro-mesh) have been used based on their structural property and biocompatibility. The proportion of degradation material in inter-mesh (69.6%) is found extremely higher than that of electro-mesh (3.22%), thus leading to higher product weight (65.50±2.31 g/m2) and thickness (0.500±0.025 mm). After 4 weeks of implantation in animal experiment, inter-mesh with surrounding tissues is observed to have higher breaking strength in tensile behavoir and better flexibility. Tissues on inter-mesh are found to grow faster with larger thickness (0.76±0.033 mm). The surface area loss of inter-mesh (2.49±0.25%) is much less than that of electro-mesh (7.49±0.63 %) within the first 2 weeks of implantation. However, the material’s degradation is accelerated after 2 weeks, leading to a higher shrinkage of 13.12±1.48 %.
Page(s): 404-410
ISSN: 0975-1025 (Online); 0971-0426 (Print)
Appears in Collections:IJFTR Vol.44(4) [December 2019]

Files in This Item:
File Description SizeFormat 
IJFTR 44(4) 404-410.pdf718.53 kBAdobe PDFView/Open

Items in NOPR are protected by copyright, with all rights reserved, unless otherwise indicated.