Title: Electrical and optical properties of n-type InSb thin films
Authors: Vishwakarma, Shree Ram
Keywords: n-InSb thin films;Temperature;Resistivity;Carrier concentration;Direct band gap
Issue Date: Sep-2016
Publisher: NISCAIR-CSIR, India
Abstract: The n-type indium antimonide thin films of the thickness 900 nm have been fabricated by electron beam evaporation technique on ultrasonically cleaned glass substrates at different temperatures (298 K–473 K) using optimized source material. The electrical and optical properties of these films have been studied and optimized the film deposition temperature. The electrical resistivity decreases (1.50-0.25)×10-3 with increase of temperature up to 398 K. The Hall Effect measurement indicates that the films are n-type semiconductor having carrier concentration (0.100.040)×1018 cm-3 and mobility (3.03-53.20)×104 cm2/Vs. The type of semiconductivity has also been confirmed by TEP measurement. The direct band gap has been calculated by Fourier Transform Infrared (FTIR) transmission spectra recorded at room temperature. The direct band decreases from 0.195 to 0.180 eV with increase of substrate temperatures (298 K-473 K). The carrier concentration 0.040×1018 cm-3, Hall mobility 53.20×104 cm2/Vs, electrical resistivity 0.25 ×10-3 and direct band gap 0.18 eV have been observed for n-InSb film of 900 nm thick deposited at 398 K.
Page(s): 557-561
ISSN: 0975-1041 (Online); 0019-5596 (Print)
Appears in Collections:IJPAP Vol.54(09) [September 2016]

Files in This Item:
File Description SizeFormat 
IJPAP 54(9) 557-561.pdf166.87 kBAdobe PDFView/Open

Items in NOPR are protected by copyright, with all rights reserved, unless otherwise indicated.