Title: Dielectric study of spin coated nano-thick BaZrxTi₁₋xO₃ film
Authors: Rout, S K
Badapanda, T
Panigrahi, S
Keywords: Perovskite
Dielectrics
Thin film
BaTiO₃-BaZrO₃
Grain size
Issue Date: Sep-2007
Series/Report no.: G01R27/26
Abstract: Barium zirconium titanate thin films are attractive candidates for dynamic random access memories and tunable microwave devices. Barium zirconate titanate Ba(ZrxTi₁₋x) O₃ (BZT, y = 0.0, 0.2, 0.4) ceramics have been prepared by a sol-gel process. X-ray diffraction studies confirmed that the films of BZT are in crystalline form and of single phase. The SEM study shows that the films of homogeneous microstructure and Zr content strongly influence the grain size of the film. The grain size decreased and the microstructure became dense when Zr was substituted for Ti. The room temperature dielectric study shows that the permittivity as well as dielectric loss tangent decreases with increase in Zr content in the film. The ac conductivity was evaluated from dielectric data and was found to be decrease with increase in Zr concentration.
Description: 749-753
URI: http://hdl.handle.net/123456789/2671
ISSN: 0019-5596
Appears in Collections:IJPAP Vol.45(09) [September 2007]

Files in This Item:
File Description SizeFormat 
IJPAP 45(9) 749-753.pdf435.66 kBAdobe PDFView/Open


Items in NOPR are protected by copyright, with all rights reserved, unless otherwise indicated.