dc.contributor.authorKumar, T-
dc.contributor.authorVishwanatham, S-
dc.contributor.authorEmranuzzaman-
dc.date.accessioned2008-06-09T08:49:57Z-
dc.date.available2008-06-09T08:49:57Z-
dc.date.issued2008-05-
dc.identifier.issn0971–457X-
dc.identifier.urihttp://hdl.handle.net/123456789/1451-
dc.description221-227en_US
dc.description.abstractEffects of inhibitor mixtures (TVE-3A, TVE-3B and TVE-3C) containing formaldehyde in combination with phenol or cresol on corrosion behaviour of N80 steel in 15% HCl solution were investigated using weight loss and potentiostatic polarization technique. The influence of temperature (30-115°C) and time interval (6-24 h) in the absence and presence of inhibitors on corrosion of the steel in the acid has been studied. TVE-3B has shown the maximum inhibition of 68.6% at ambient temperature whereas maximum inhibition shown by TVE-3A and TVE-3C was found to be 62.2% and 65.7% respectively. The inhibition efficiency was found to gradually decrease with increase in temperature in the case of TVE-3A while TVE-3B and TVE-3C showed a further increase in the protection at higher temperatures (about 81% at 115°C). The protective efficiency of TVE-3B and TVE-3C is comparable with Grade-III (about 88% at 115°C) commercial inhibitor. Inhibition of corrosion is due to adsorption of inhibitors on the metal surface. The adsorption is found to obey Frumkin isotherm. FTIR study of the metal surface products after the corrosion inhibition tests reveal presence of non-linear poly phenyl species, no free carbonyl group indicating formation of a cross linked and three dimensional networking resulting in novalac resin or bakelite by condensation polymerization (acid catalyzed). Oxygen atom, (of –OH group in phenol or substituted phenol) may coordinate to Fe²⁺ on the metal surface resulting in a protective inhibitor layer. Thermal stability of the inhibitor mixtures was determined by DSC, which has shown that the compounds present in TVE-3A vaporize with increase in temperature while the compounds present in the case of TVE-3B and TVE-3C are thermally stable up to 200°C.en_US
dc.language.isoen_USen_US
dc.publisherCSIRen_US
dc.sourceIJCT Vol.15(3) (May 2008)en_US
dc.subjectCorrosion inhibitoren_US
dc.subjectN80 Steelen_US
dc.subjectPhenolen_US
dc.subjectCresolen_US
dc.titleStudy on corrosion control of N80 steel in acid medium using mixeden_US
dc.typeArticleen_US
Appears in Collections:IJCT Vol.15(3) [May 2008]

Files in This Item:
File Description SizeFormat 
IJCT 15(3) (2008) 221-227.pdf239.95 kBAdobe PDFView/Open


Items in NOPR are protected by copyright, with all rights reserved, unless otherwise indicated.