dc.contributor.authorVishwanatham, S-
dc.contributor.authorHaldar, Nilesh-
dc.description.abstractThe inhibitory action of methoxy phenol (MPH) and nonyl phenol (NPH) on corrosion of N80 steel in 15% HCl has been investigated at different period of exposure (6 to 24 h) and temperature (30 to 110°C). Nonyl phenol and methoxy phenol have shown maximum inhibition of about 83 and 78% at 75 mM inhibitor concentration in the acid respectively after 6 h exposure test at ambient temperature. The inhibition efficiencies of nonyl phenol and methoxy phenol are found to be about 79 and 30% respectively after 24 h exposure. Nonyl phenol has shown maximum inhibition of about 59 and 44% at 75 mM inhibitor concentration in the acid respectively at 90 and 110°C respectively. The inhibition afforded by methoxy phenol was found to be relatively low (about 34% at 60°C). Heat of adsorption was found to be 50 KJ/mol in case of MPH, indicating formation of a protective chemisorbed film on the metal surface, which suppresses the dissolution reaction. NPH showed heat of adsorption of about 26 KJ/mol indicating a weak chemisorption. Both these compounds inhibit corrosion by adsorption mechanism and follow Temkin isotherm. The results of polarization studies indicate that the compounds are mixed type inhibitors. The FTIR spectral analyses of the surface product suggest involvement of hydroxyl group (un protonated as well as protonated) of these inhibitor molecules in the adsorption process.en_US
dc.sourceIJCT Vol.14(5) [September 2007]en_US
dc.subjectCorrosion inhibitionen_US
dc.titleCorrosion inhibition of N80 steel in hydrochloric acid by phenol derivativesen_US
Appears in Collections:IJCT Vol.14(5) [September 2007]

Files in This Item:
File Description SizeFormat 
IJCT 14(5) (2007) 501-506.pdf160.08 kBAdobe PDFView/Open

Items in NOPR are protected by copyright, with all rights reserved, unless otherwise indicated.